diff --git a/3683/CH18/EX18.4/Ex18_4.sce b/3683/CH18/EX18.4/Ex18_4.sce new file mode 100644 index 000000000..b2960c1f4 --- /dev/null +++ b/3683/CH18/EX18.4/Ex18_4.sce @@ -0,0 +1,33 @@ +b=300//in mm
+D=400//in mm
+c=30//cover, in mm
+Asc=452//in sq mm
+Ast=Asc
+fck=15//in MPa
+fy=415//in MPa
+fcc=0.446*fck//in MPa
+//(i)
+xu=1.4*D//in mm
+m=0.43*D//in mm
+esc1=0.002*(xu-c)/(xu-m)
+esc2=0.002*(xu-D+c)/(xu-m)
+//by interpolation
+fsc1=356.8//in MPa
+fsc2=238.68//in MPa
+//stress block parameters for xu / D = 1.4
+n=0.417
+l=0.475
+A=n*fck*D//area of stress block
+r=l*D//distance of c.g., in mm
+Pu=(A*b+Asc*(fsc1-fcc)+Ast*fsc2)/10^3//in kN
+Mu=(A*b*(D/2-r)+Asc*(fsc1-fcc)*(D/2-c)-Ast*fsc2*(D/2-c))/10^6//in kN-m
+mprintf("(i) For xu = 1.4 D\nP=%f kN\nMu=%f kN-m\n",Pu,Mu)
+//(ii)
+xu=370//in mm
+esc=0.0035*(xu-c)/xu
+est=0.0035*(D-c-xu)/xu
+//by interpolation
+fsc=355.8//in MPa
+Pu=(0.36*fck*b*xu+Asc*(fsc-fcc))/10^3//in kN
+Mu=(0.36*fck*b*xu*(D/2-0.416*xu)+Asc*(fsc-fcc)*(D/2-c))/10^6//in kN-m
+mprintf("(ii) For xu = 370 mm\nP=%f kN\nMu=%f kN-m",Pu,Mu)
|